DIMONDS® P1814/PIR HFC-blown Blend Polyols for PIR Foam Discontinuous Sandwich Panel

Short Description:

Description DIMONDS® P1814/PIR is a type of blend polyols developed for discontinuous panel. It is developed using HFC-245fa as blowing agent which contains polyether polyol, silicone surfactant, catalysts, flame retardant and other special additives etc. It has good flowability and flammability compared with PUR foam. Typical Properties Item Unit DIMONDS® P1814/PIR DIMONDS® ISO1800 Physical state Appearance Transparent liquid Brown liquid Viscosity, 25℃ mpa.s 300-500 150-250 Grav...

FOB Price: US $2.0 - 4.0/Kg

Min.Order Quantity: 1000 Kg

Supply Ability: 1000 MT per Month

Send email to us Download as PDF

Product Detail

Product Tags

Description

DIMONDS^® P1814/PIR is a type of blend polyols developed for discontinuous panel. It is developed using HFC-245fa as blowing agent which contains polyether polyol, silicone surfactant, catalysts, flame retardant and other special additives etc. It has good flowability and flammability compared with PUR foam.

Typical Properties

Item	Unit	DIMONDS^® P1814/PIR	DIMONDS^® ISO1800
Physical state	Appearance	Transparent liquid	Brown liquid
Viscosity, 25℃	mpa.s	300-500	150-250
Gravity,20℃	g/ml	1.15±0.05	1.24±0.01

Reaction properties (hand test)

Item	Unit	Specification
Cream time	sec	15-30
Gel time	sec	100-180
Free rise density	kg/m3	27-29

Processing information

Item	Unit	Specification
Component temperature	℃	22±3
Mold temperature	℃	55±3
Dynamic pressure	kPa	125±10
Demold time	Min	>30

It is recommended to utilize high pressure foaming machinery. The chemicals should be adjusted to the correct temperature between 20-24℃ to ensure reactivity and viscosity suitable for processing.

The mixing pressure has to be set for both components at 120-130 bar.

The mould temperature recommended is 50-55℃ to guarantee good foam performances.

Foam properties

Item	Unit	Specification	Test standard
Core density	kg/m3	≥40	ASTM D1622-08
Thermal conductivity, 20℃	W/(m.k)	≤0.024	ASTM C518-10
Compressive strength	kPa	≥140	ASTM D1621-10
Closed cell content	%	≥90	ASTM D6226
Water absorb	%	≤3	ASTM C209-12
Thermal stability, -30-80℃	%	≤1.5	ASTM D2126-09
Flammability		B2	DIN 4102

The above testing data have been generated in lab or field conditions which are typical for this application. They are believed to be correct but data variations due to varying processing or ambient conditions can not be excluded. The customer remains responsible for making his own interpretation of data and suitability of the chemicals to his particular operation.

Handling and Storage

DIMONDS^® P1814/PIR should be protected from moisture by keeping containers sealed when not in use. Drums have to be stored indoors to protect the material from water ingress, frost and direct heat from the sun. Under temperature conditions and in properly sealed containers ,the storage life of the polyol is 6 months.

The optimum storage temperature should be 10-30℃.

Package

220kg/drum or 1200kg/IBC for polyol, 250kg/drum or 1250kg/drum for isocyanate.

Previous: DIMONDS® P1814 HFC-blown Blend Polyols for PU Foam Discontinuous Sandwich Panel

Next: DIMONDS® P1822/PIR Blend Polyols for PIR Foam Continuous Sandwich Panel

Write your message here and send it to us